Functional Materials 5,No.4(1998)

Precision X-ray diffraction analysis together with scanning electron microscopy, electron microprob and thermal analysis have been used thermal decomposition of barium-yttrium cuprat YBa₂Cu₃O_х above 900 ⁰C in two ambients: fir and vacuum (residual p(0₂)=700 Pa). In air,YBa₂Cu₃O_х undergoes pritectic decomposition at 1020 ⁰C into Y₂BaCuO₅ and melt of barium and monovalent copper oxides. Y₂BaCuO₅ remains stable up to 1270⁰C and at that temperature decomposes to Y₂O₃. In vacuum, at p(O₂)=700 Pa, complete peritectic decomposition of 123 phase takes place at 965⁰C and is preceded, starting from 925⁰C, by nonequilibrium partial decomposition of YBa₂Cu₃O_х into Y₂BaCuO₅, YBa₃Cu₂O_y and BaCu₂O₂.

Методами прецизионной рентгенографии, сканирующей электронной микроскопии, локального электроннозондового и термического анализа изучены термические превращения при нагревании YBa₂Cu₃O_х выше 900 ⁰C по двум изобарам: на воздухе и в вакууме при p(0₂)=700 Па. На воздухе YBa₂Cu₃O_х претерпевает перетектический распад при 1020⁰C на Y₂BaCuO₅ и расплав оксидов бария и одновалентной меди. Фаза Y₂BaCuO₅ остается устойчивой до 1270⁰C, после чего подвергается перетектическому разложению до Y₂O₃. В вакууме при p(O₂)=700 Па полный перетектический распад происходит при более низкой температуре 965⁰C и ему предшествует, начиная с 925⁰C, неравновесное частичное разложение фазы YBa₂Cu₃O_х до Y₂BaCuO₅, YBa₃Cu₂O_y и BaCu₂O₂.